Incoloy 901
|
GH2901
|
W.Nr.2.4662
|
合金
|
C
|
Mn
|
Si
|
P
|
S
|
Cr
|
Ni
|
Mo
|
Cu
|
Ti
|
Al
|
Fe
|
其他
|
Incoloy 901
|
≤0.1
|
≤1
|
≤0.6
|
≤0.03
|
≤0.03
|
11
~14 |
40
~45 |
5
~6.5 |
≤0.5
|
2.8
~3.1 |
≤0.35
|
余量
|
B 0.01~0.02
Co≤1 |
密度
|
8.14g/cm3
|
熔点
|
1280-1345℃
|
合金
|
抗拉强度
Rm N/mm2 |
屈服强度
RP0.2N/mm2 |
延伸率
A5 % |
Incoloy 901
|
1034
|
689
|
12
|
θ/℃
|
σЬ/ MPa
|
σ0..2/ MPa
|
δ5/%
|
Ψ/%
|
20
|
1130
|
810
|
9
|
12
|
575
|
960
|
690
|
8
|
-
|
θ/℃
|
氧化速率/(g/m2·h)
|
600
|
0.0072
|
700
|
0.0140
|
800
|
0.0522
|
900
|
0.1665
|
1000
|
0.02367
|
Θ/℃
|
λ/(W/(m·℃)
|
100
|
12.0
|
200
|
13.5
|
300
|
15.1
|
400
|
16.7
|
500
|
18.2
|
600
|
19.8
|
700
|
21.2
|
800
|
22.8
|
900
|
24.3
|
1000
|
25.1
|
Θ/℃
|
α/10-6℃-1
|
20-100
|
13.5
|
20-200
|
14.0
|
20-300
|
14.4
|
20-400
|
14.9
|
20-500
|
15.1
|
20-600
|
15.2
|
20-700
|
15.5
|
20-800
|
16.0
|
20-900
|
16.5
|
Θ/℃
|
Q/(10-6m2/s)
|
20
|
2.66
|
100
|
2.93
|
150
|
3.00
|
250
|
3.18
|
350
|
3.47
|
450
|
3.73
|
550
|
3.78
|
650
|
4.02
|
950
|
4.11
|
Θ/℃
|
ρ/(10-6Ω·m)
|
20
|
1.073
|
100
|
1.095
|
200
|
1.132
|
300
|
1.162
|
400
|
1.199
|
500
|
1.229
|
600
|
1.254
|
700
|
1.275
|
800
|
1.309
|
900
|
1.316
|
θ/℃
|
σ/ MPa
|
t/h
|
εt/%
|
εtp/%
|
550
|
588
|
100
|
0.3180-0.3850
|
0.0160-0.067
|
650
|
490
|
100
|
0.3945-0.5615
|
0.0935-0.1930
|
750
|
186
|
100
|
0.1395-0.1525
|
0.0235-0.0550
|
θ/℃
|
循环周期
|
裂纹长度
|
备注
|
750↔20
|
30
|
0.27-0.48
|
实验150周后未发现裂纹
|
600
|
0.67-1.00
|
Θ/℃
|
ED/GPa
|
20
|
200
|
100
|
200
|
200
|
194
|
300
|
186
|
400
|
179
|
500
|
174
|
600
|
167
|
700
|
160
|
800
|
150
|
900
|
144
|